hrc 58 65 hard overlay welding wear plates
Different chromium carbide overlay wear plates have different hardness levels. The hardness would depend on a wide range of factors, such as the heat treatment, the material used, and many more. On average, the hardness levels of chromium carbide overlay or CCO wear plates are usually around 59 to 64 HRC.
ABRAPLATE®, ERGOTEMs bi-metallic wear plate, is a unique chromium carbide overlay plate on a mild steel base.Its excellent wear and abrasion resistant properties ensure extended service life of equipment, while reducing maintenance costs. ABRAPLATE® is produced by a unique and versatile automatic bulk welding method, using the highest quality raw materials offering superior wear Hard Facing Wear Resistant Steel Plate with High Quality Chemical composition:hardfacing overlay steel plate are manufactured by welding one or multiple abrasion resistant layers on Mild steel (Q235, Q345) or stainless steel (SS 304, SS 309, SS 310) base plate. The overlay alloy has a high amount of chromium carbide hard particles.
Chromium Carbide Overlay Wear Plate, Flux Cored Welding Wire, Wear Resistant Liner manufacturer / supplier in China, offering Hardfacing Abrasion Alloy Wear Resistant Plate, Bimetal Carbide Wear Plate, Wodon Wear Resistant Overlay Flux Cored Welding Wire and so on. HRC 58-65 Chromium Carbide Hard Plate. FOB Price:US $110-470 / Square Meter High Hardness 58-63 Hrc Wear Resistant Composite Welded High Hardness 58-63 Hrc Wear Resistant Composite Welded Wear Steel Plate , Find Complete Details about High Hardness 58-63 Hrc Wear Resistant Composite Welded Wear Steel Plate,Wear Resistant Plate,Composite Plate,Welded Plate from Steel Sheets Supplier or Manufacturer-Tianjin Wodon Wear Resistant Material Co., Ltd.
OVERLAY-PLATE is welded by Chromium carbide overlay on a mild steel backing plate. Manufactured by our own design's welding machine with exclusive technique. 1) HYSTER OVERLAY-W Series Chromium Carbide Compound Plate(EQUAL TO BRADKEN D60) Chemical Composition:C 3.5% , Cr 20%, Mn, Si, Fe. Hardness:HRC 58-62. REPAIR AND MAINTENANCE WELD OVERLAY 63-65 HRC UTP LEDURIT 65 Excellent wear resistance to fine abrasive particles of high hardness. Working temperature up to 500 °C. Surfacing on earth moving equipment,scraper bars, wear bars and plates. 63 HRC Diadur HR SK 900-O The cored wire containing about 60% and the electrode about 45% Tungsten carbide particles.
Submerge arc welding CCO plate. Supported by patent technique, Waldun brand submerge arc welding chromium carbide overlay wear plate has become the representitive of high quality wear plates, well known for its superior abrasion and impact resistance. It is manufactuered under tightly controlled parameters within a quality management system. WAG Composite Plates - Welding Alloys - Welding ASTM G-65 wear test performed by an independent laboratory. The results compare the wear life of various products tested, with Welding Alloys composite overlay plates proving they provide superior wear protection. As an example, Hardplate 100 has outlasted 500 BHN quenched and tempered material by a factor of 4 and Hardplate 300, by a
HRC 58-63:1400*3400/1500*3000: Carbon and Chromium content varies in different plate thickness. W D1200/WD1500 series:High chromium high carbon wear plates produced by submerged arc welding; Suited for applications involving severe abrasion and low to medium impact. Wodon brand chromium carbide overlay clad plates have become the